| Effect and characteristics of alloy components » | ||||||||||||
| Solder | Order No. | Composition % by mass | Other elements |
Colour code |
Working temperature [°C] |
|||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Au | Pt | Pd | Ag | Cu | Sn | Zn | In | |||||
| BEGO-Gold-Lot I | 61017 | 73,0 | - | - | 9,5 | 12,5 | 2,0 | 2,9 | 0,1 | - | 2 | 810 |
| BEGO-Gold-Lot II | 61043 | 61,0 | - | - | 13,0 | 18,0 | 3,5 | 4,4 | 0,1 | - | 3 | 765 |
| BegoStar®-Lot | 61081 | 55,0 | - | 10,0 | 34,0 | - | - | - | 1,0 | - | 8 | 1125 |
| Bio PlatinLloyd®-Lot before firing |
61108 | 90,7 | 2,0 | - | - | - | - | 7,2 | - | Ir 0,1 | 3 | 870 |
| Bio PlatinLloyd®-Lot after firing |
61109 | 68,5 | 1,6 | - | 13,8 | - | - | 16,0 | - | Ir 0,1 | 6 | 710 |
| Gold-EWL®-Lot I | 61066 | 12,0 | - | 16,0 | 51,0 | 15,0 | 2,4 | 3,5 | 0,1 | - | 8 | 910 |
| Gold-EWL®-Lot II | 61067 | 15,0 | - | 14,0 | 43,0 | 19,0 | 3,5 | 5,0 | 0,5 | - | 8 | 820 |
| PontoLloyd®-Lot | 61074 | 80,0 | 1,5 | 5,5 | 11,5 | 0,5 | 0,9 | - | 0,1 | - | 7 | 1120 |
| PontoRex®-Lot before firing |
61038 | 76,0 | 2,9 | - | 10,0 | 6,0 | - | 5,0 | - | Ir 0,1 | 2 | 880 |
| PontoRex®-Lot after firing |
61039 | 72,5 | 0,5 | - | 10,0 | 3,0 | - | 11,9 | 2,0 | Ir 0,1 | 2 | 710 |
| PontoStar®-G-Lot | 61045 | 64,0 | 0,4 | - | 34,8 | - | - | - | 0,6 | Rh 0,2 | 2 | 1030 |
| Pre-flux U Goldlot with integrated flux |
61028 | 73,0 | - | - | 9,5 | 12,5 | 1,9 | 3,0 | 0,1 | - | 2 | 810 |
| The specified data are standard values. Subject to change. | ||||||||||||
BEGO-GOLD alloys and solders are medical devices in accordance with Regulation 93/42 EEC.
According to Annex IX, the products are classified in Class IIa.